Odredivanje parametara zavarivanja celika za poboljsavanje

Dunđer, Marko (1997) Odredivanje parametara zavarivanja celika za poboljsavanje. = Welding parameters determinations in steels for hardening and tempernig. Scientific master's thesis , Sveučilište u Zagrebu, Fakultet strojarstva i brodogradnje, UNSPECIFIED. Mentor: UNSPECIFIED.

Full text not available from this repository.

Abstract (Croatian)

Za pouzdan rad proizvoda iz raznih vrsta čelika potrebno je kvalitet osigurati pravilnim određivanjem parametara i slijeda zavarivanja. U radu je istraživana sklonost čelika za poboljšavanje hladnim pukotinama koje nastaju uslijed zavarivanja. Kako proces zavarivanja predstavlja specifičan oblik nastajanja temperaturnog polja, teorijski je razrađeno određivanje temperaturnih polja pri zavarivanju. Pomoću Implant i Tekken-metode ispitivanja sklonosti hladnim pukotinama, određeni su parametri pri kojima se postiže dobra zavarljivost, tj. zavar bez hladnih pukotina. Pri eksperimentalnim ispitivanjima korišten je konstantan unos topline od 17 kJ/cm za maksimalnu temperaturu predgrijavanja, a temperatura predgrijavanja je bila promjenjiva. Probe su zavarivane REL i MAG postupkom zavarivanja, uz korištenje dodatnog materijala proizvođača "Elektroda" Zagreb i "železarna" Jesenice. Pokusi su provedeni na dvije vrste čelika: - niskolegiranom krom-molibdenskom čeliku 25 CrMo 4, - nelegiranom ugljičnom čeliku Ck 45. Na temelju dobivenih rezultata mote se zaključiti da su oba čelika sklona hladnim pukotinama, a da bi se pukotine spriječile, koristit ce se parametri dani u radu.

Abstract

In order to archieve reliable products made from various types of steel the right welding parame¬ters and methods must be used. This work describes experimental research into those types of steel for structural improvement whic tend to develop cold cracks when welded. Since welding creates specific temperaturs zones, the experiment was designed to determine these temperature zones during the welding process. The Implant and Tekken methods made it possible to determine the parameters required to achieve good weldability without cold cracks in those steels that tend to produce them. In the experiment samples were exposed to a continual heat transfer as high as 17 kJ/cm in order to achieve the maximum pre-heating temperature. The pre-heating temperature did in fact fluctuate. The samples were welded using the REL and MAG methods and additional materials manufac¬tured by ""Elektroda"", Zagreb and ""Zelezarna"", Jesenice. Two types of steel were used: - low-alloy steel chrom-molibden 25 CrMo 4 - non-alloy carbon steel Ck45 Results showed that both the above types are inclined to cold cracks but that cracking can be prevented by applying the parameters described in this work.

Item Type: Thesis (Scientific master's thesis)
Uncontrolled Keywords: zavarljivost; temperaturna polja; parametri zavarivanja; hladne pukotine; čelici za poboljšavanje
Keywords (Croatian): weldability; temperature range; welding parameters; cold cracks; steels for structural improvement