Pugar, Daniel (2014) Analiza svojstva i primjene APM pjena. = Analysis of properties and application of APM foam. Master's thesis (Bologna) , Sveučilište u Zagrebu, Fakultet strojarstva i brodogradnje, UNSPECIFIED. Mentor: Marić, Gojko.

[img] Text
10_07_2014_Daniel_Pugar_-_Diplomski_rad.pdf
Restricted to IP adress Jezik dokumenta:English

Download (5MB)

Abstract (Croatian)

Svojstva koja posjeduju metalne pjene (niska gustoća, apsorpcija energije, prigušenje vibracija i zvuka) teško je bilo ostvariti u stvarnim životnim proizvodima. \Napredne (APM) aluminijske pjene predstavljaju potpuno novi materijal i novi pojednostavljeni proces proizvodnje, usmjeren isključivo na ispunjavanje šupljih dijelova pjenom (npr. u autoindustriji). APM pjene izrađene su od kuglica pjene, malog volumena, međusobno spojenih u odvojenom koraku procesa. Spajanje kuglica pjene sa ljepilom rezultira kompozitnom pjenom s oko 80-95 % težine aluminijske pjene i 5-20 % težine ljepila. Uspostavljanje ćelijaste strukture od kuglica pjene omogućuje automatizaciju proizvodnje dijelova, dobru kontrolu pora i isplativu primjenu aluminijskih pjena. U prvom dijelu rada ukratko su opisane APM pjene, njihova struktura, te postupak proizvodnje. Također su navedena najvažnija područja primjene, te prednosti u usporedbi s konvencionalnom metalnom pjenom. Cilj eksperimentalnog dijela rada bio je ispitati mehanička svojstva hibridne APM pjene kao ispune za šuplje konstrukcije. Za usporedbu su napravljeni uzorci kod kojih je šuplja konstrukcija ispunjena sa konvencionalnom pjenom, uzorci ispunjeni samo sa polimernim vezivom, te uzorci bez ispune. \Na ispitnim uzorcima je provedeno savojno i tlačno ispitivanje kako bi se utvrdio utjecaj različitih ispuna na mehanička svojstva šupljih konstrukcija. Rezultati ispitivanja prikazani su tablično i grafički.

Abstract

Unique properties of closed cell metal foams (low density, efficient energy absorption, high vibration/sound attenuation) in real life products has often been difficult to realise. With advanced pore morphology (APM) aluminium foam–polymer hybrids a new and simplified process route targeted at application in foam-filled structures (e.g. in automotive) has been introduced. APM foams are made from spherical, small volume foam elements joined to each other in a separate process step. Joining the aluminium foam elements by adhesive bonding delivers composite foam with approximately 80–95 wt.% aluminium foam and 5–20 wt.% adhesive (polymer). Setting up cellular structures from spherical foam elements allows for automatic part production, good pore morphology control and cost effective aluminium foam application. In the first part of work, shortly are presented APM foams, their structure and the manufacturing process. Also are listed the most important areas of application and advantages in comparison with conventional metal foam. The aim of the experimental part was to investigate the mechanical properties of hybrid APM foam as filling for hollow structures. For comparison, samples were made in which the hollow structure was filled with conventional foam, samples filled only with adhesive polymer, and samples without filling. The test samples were subjected to flexural and compressive testing to determine the impact of different fillings on the mechanical properties of hollow structures. The results of testing are demonstrated in the table chart and graphically.

Item Type: Thesis (Master's thesis (Bologna))
Uncontrolled Keywords: metalne pjene; APM tehnologija; šuplje konstrukcije; epoksidna smola
Keywords (Croatian): metal foams; APM technology; hollow structures; epoxy resin
Divisions: 1000 Department of Materials > 1010 Chair of Materials and Tribology
Date Deposited: 22 Sep 2014 18:00
Last Modified: 16 Oct 2015 12:48
URI: http://repozitorij.fsb.hr/id/eprint/2812

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

Nema podataka za dohvacanje citata