Analiza materijala cijevi streljačkog oružja

Sedak-Benčić, Ivan (2014) Analiza materijala cijevi streljačkog oružja. = Analysis of small arms barrel material. Master's thesis (Bologna) , Sveučilište u Zagrebu, Fakultet strojarstva i brodogradnje, UNSPECIFIED. Mentor: Jakopčić, Mirko.

[img]
Preview
Text
10_07_2014_Diplomski_rad-Ivan_Sedak-Bencic.pdf Jezik dokumenta:English

Download (11MB) | Preview

Abstract (Croatian)

Cijev je glavni dio vatrenog oružja. Ona je nositelj procesa opaljenja i najopterećeniji je dio vatrenog oružja. Tijekom izgaranja barutnog punjenja, te kretanja projektila kroz cijev, unutar volumena cijevi dolazi do oslobađanja visokih temperatura i tlakova uslijed čega nastaju visoka toplinska i mehanička opterećenja cijevi. Kod nekontroliranog režima paljbe na cijevi mogu nastati razna oštećenja, bilo od toplinskog umora, visokog tlaka, ili povećanog trošenja kao posljedice pada tvrdoće cijevi. U ovom radu ispitivane su cijevi od tri različite vrste streljačkog oružja. Cilj ispitivanja je bio određivanje promjena mehaničkih svojstava cijevi koje nastaju pri različitim visinama temperaturnog opterećenja kroz vrijeme od 1 h. Cijevi su se toplinski opterećivale u peći za toplinsku obradu na temperaturama od 600°-1000°C, te su hlađene na zraku pri čemu su se oponašali stvarni uvjeti koji nastaju u cijevi prilikom paljbe. Analiziran je kemijski sastav, te promjene mikrostrukture i tvrdoće koje nastaju pri različitim temperaturama toplinskog opterećenja. Konačno su prikazani rezultati analize, te je dan zaključak.

Abstract

The barrel is the main part of the firearm. It is responsable for the process of firing and it is the most loaded part of the firearm. During the combustion of gunpowder, and the movement of the projectile through the barrel, the volume inside the barrel comes to the release very high temperatures and pressures which occur due to high thermal and mechanical loads of the barrel. Uncontrolled fire regimes in barrel can cause a variety of damage, either from thermal fatigue, high mechanical pressure, or increased wear as a result of the fall of hardness. This paper shows the analysis of three different types of firearm barrels. The aim of the study was to determine the changes in the mechanical properties of the barrels that are formed at different heights of the temperature load for a period of 1 h. The barrels are heated in furnaces at temperatures of 600 °-1000 ° C, and are cooled by the air in which they simulated the actual conditions occurring in the barrel during firing. We analyzed the chemical composition, microstructure and hardness changes that occur at different temperatures heat load. Finally the results of the analysis and the conclusion are given.

Item Type: Thesis (Master's thesis (Bologna))
Uncontrolled Keywords: oružje; cijev vatrenog oružja; proces opaljenja; analiza materijala cijevi
Date Deposited: 22 Sep 2014 18:00
Last Modified: 16 Oct 2015 12:48
URI: http://repozitorij.fsb.hr/id/eprint/2814

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

Nema podataka za dohvacanje citata