Tribološka svojstva kompozitne Al2O3 – ZrO2 keramike

Sakoman, Matija (2014) Tribološka svojstva kompozitne Al2O3 – ZrO2 keramike. = Tribological properties of composite Al2O3 – ZrO2 ceramics. Master's thesis (Bologna) , Sveučilište u Zagrebu, Fakultet strojarstva i brodogradnje, UNSPECIFIED. Mentor: Grilec, Krešimir.

[img] Text
10_07_2014_Matija_Sakoman_-_Diplomski_final.pdf
Restricted to Repository staff only Jezik dokumenta:English

Download (3MB)

Abstract (Croatian)

U ovom radu postupkom lijevanja u gipsani kalup proizvedeni su uzorci monolitne Al2O3 i kompozitne Al2O3-t-ZrO2 (sastava 95 % Al2O3 – 5 % t-ZrO2 i 90 % Al2O3 – 10 % t-ZrO2) keramike. Otpornost na erozijsko trošenje sinteriranih uzoraka monolitne (Al2O3) i kompozitne (Al2O3−t-ZrO2) keramike određena je: (i) SEM analizom morfologije površine uzoraka prije i poslije trošenja, (ii) mjerenjem parametara hrapavosti (Ra, Rmax, Rz) prije i poslije trošenja,te (iii) mjerenjem mase uzoraka prije i poslije trošenja pri različitom kutu (30°, 60° i 90°) upada erodenta (SiC). Dobiveni rezultati pokazuju da vrijednosti parametara hrapavosti (Ra, Rz i Rmax,) rastu nakon erozijskog trošenja, a najveći porast zabilježen je za monolitnu Al2O3 keramiku. Promjena vrijednosti parametara hrapavosti smanjuje se s porastom udjela ZrO2 u kompozitnoj keramici. Analizom morfologije površine nakon trošenja vidljivo je da su tragovi trošenja na površini monolitne Al2O3 keramike znatno veći nego na površini kompozitne Al2O3–t-ZrO2 keramike, a što je u skladu s izmjerenim parametrima hrapavosti. Za sve uzorke gubitak mase je najmanji pri kutu upada erodenta od 30°, a najveći pri kutu od 90°. Rezultati ispitivanja pokazuju dva do tri puta manji gubitak mase kod uzoraka s dodatkom ZrO2 kod svih kutova udara erodenta. Sva provedena ispitivanja pokazuju da se tribološka svojstva monolitne Al2O3 keramike mogu poboljšati dodatkom t-ZrO2 keramike.

Abstract

In this paper slip casting procedure was used to produce samples of monolytic Al2O3 and composite Al2O3-t-ZrO2 (with 95 % Al2O3 – 5 % t-ZrO2 and 90 % Al2O3 – 10 % t-ZrO2) ceramics. Erosive wear resistance of sintered monolithic Al2O3 and composite Al2O3–t-ZrO2 ceramics was determined by: (i) SEM analysis of the sample surface morphology before and after erosion, (ii) measuring of the roughness parameters (Ra, Rmax, Rz) before and after erosion, and (iii) measuring the sample mass before and after erosion at different impact angle (30°, 60° and 90°) of erodent particles (SiC). Obtained results indicated that values of roughness parameters (Ra, Rz and Rmax,) increased after erosion, and the largest increase was observed for monolithic Al2O3 ceramics. Surface roughness parameter values decrease with the increase of ZrO2 amount. Surface morphology analysis after erosion showed that wear scars were significantly larger on Al2O3 than on Al2O3–t-ZrO2 samples, which is in agreement with decreased roughness parameters. The weight loss was lowest at the erodent impact angle of 30° and highest at 90° for all samples. Obtained results showed two to three times lower weight loss for the sample containing ZrO2 at all erodent impact angles. All conducted tests showed that tribological properties of monolithic Al2O3 can be improved with the addition of t-ZrO2.

Item Type: Thesis (Master's thesis (Bologna))
Uncontrolled Keywords: Al2O3; Al2O3–t-ZrO2; lijevanje suspenzije viskoznost; erozija česticama
Keywords (Croatian): Al2O3; Al2O3–t-ZrO2; slip casting; viscosity; solid particle erosion
Date Deposited: 22 Sep 2014 18:00
Last Modified: 16 Oct 2015 12:48
URI: http://repozitorij.fsb.hr/id/eprint/2815