Pavković, Marko (2014) Utjecaj vode i UV zračenja na dinamičko-mehanička svojstva biaksijalno orijentiranog etilen/vinil-alkoholnog kopolimera. = Effect of water and UV radiation on dynamic-mechanical properties of biaxially oriented ethylene-vinyl alcohol copolymer. Master's thesis (Bologna) , Sveučilište u Zagrebu, Fakultet strojarstva i brodogradnje, UNSPECIFIED. Mentor: Haramina, Tatjana.

[img] Text
10_07_2014_Diplomski_rad_Pavkovic_Marko.pdf
Restricted to IP adress Jezik dokumenta:English

Download (2MB)

Abstract (Croatian)

Ispitivanje dinamičkih svojstava polimernih materijala važan je faktor za predviđanje ponašanja materijala u radnoj okolini. Analizom dobivenih rezultata moguće je otkriti uzrok ponašanja polimera pri određenim temperaturama. Izlaganje polimera uvjetima povišene vlažnosti i ultraljubičastog zračenja vrlo je često pri eksploataciji. U takvim uvjetima moguća je promjena ponašanja materijala. Zbog toga je poželjno materijal ispitivati u uvjetima približnim onim uvjetima okoline u kojoj se materijal primjenjuje. U radu je opisan utjecaj vode i ultraljubičastog zračenja na dinamička svojstva biaksijalno orijentiranih folija. \Na primjeru EVOH folije, izmjerene su vrijednosti kompleksnog modula elastičnosti i faktora gubitka. Uzorci su ispitivani dinamičkim rasteznim opterećenjem na uređaju za dinamičko – mehaničku analizu (DMA) i to u smjeru prerade, okomito na smjer prerade i pod kutem od 45°. Dinamička opterećenja provedena su na temperaturnom intervalu od -150 do 130 °C, frekvencijom 1 Hz. Analiza folija tretiranih vodom načinjena je prije i poslije jednomjesečnog držanja folija u vodi. Ispitivanje folija tretiranih UV zračenjem provedeno je prije i poslije izlaganja zračenju u trajanju od 30, odnosno 45 minuta.

Abstract

Testing of dynamic mechanical properties is an important factor for prediction of materials behavior in actual use conditions. The analysis of the results can reveal the reasons for materials behavior on a wide temperature range. Polymeric materials are often exposed to humid and UV radiation. Under these conditions, a material can undergo changes in its behavior. Hence, it is always desirable to test material under the conditions similar to those when a material is used. In this work impact of water and ultraviolet radiation on dynamic properties of biaxial oriented films was analysed. On an example of EVOH films, complex modulus and loss factor are measured. Samples are tested on dynamic – mechanical analysis (DMA) machine under tensile stress in the machine direction, the transverse direction and under 45° to the machine direction. Dynamic loads are performed on temperature interval from -150 to 130 °C. Frequency of the dynamic load was 1 Hz. The films were exposed to water for one month, wheres the irradiation time was 30 min and 45 min.

Item Type: Thesis (Master's thesis (Bologna))
Uncontrolled Keywords: dinamičko-mehanička analiza (DMA); biaksijalna orijentacija; utjecaj vode; utjecaj UV zračenja; EVOH polimerne folije
Keywords (Croatian): dynamic – mechanical analysis (DMA); biaxial orientation; water impact; UV radiation impact; EVOH polymeric films
Date Deposited: 22 Sep 2014 18:00
Last Modified: 16 Oct 2015 12:48
URI: http://repozitorij.fsb.hr/id/eprint/2845

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

Nema podataka za dohvacanje citata