Utjecaj cijepljenja na promjenu metalografskih i mehaničkih svojstava nodularnog lijeva

Tolić, Anto (2014) Utjecaj cijepljenja na promjenu metalografskih i mehaničkih svojstava nodularnog lijeva. = Influence of inoculant type on the microstructure and mechanical properties of ductile iron. Master's thesis (Bologna) , Sveučilište u Zagrebu, Fakultet strojarstva i brodogradnje, UNSPECIFIED. Mentor: Bauer, Branko.

[img] Text
DIPLOMSKI RAD.pdf - Published Version
Restricted to Repository staff only Jezik dokumenta:Croatian

Download (4MB)

Abstract (Croatian)

U okviru ovog rada ispitivan je utjecaj cijepljenja na promjenu metalografskih i mehaničkih svojstava nodularnog lijeva kvalitete EN – GJS – 400 – 15. Za potrebe ispitivanja pripremljene su tri različite ispitne taljevine nodularnog lijeva. Za pripremu prve ispitne taljevine nodularnog lijeva korišten je samo nodulator Elmag 3717®, dok je za pripremu druge ispitne taljevine uz nodulator Elmag 3717® korišteno i cjepivo Ultraseed® Ce, a za dobivenje treće ispitne taljevine nodularnog lijeva uz spomenuti nodulator korišteno je i cjepivo Barinoc®. Rad se sastoji od teorijskog i eksperimentalnog dijela. U teorijskom dijelu rada ukratko su objašnjena svojstva, primjena i kontrola kvalitete nodularnog lijeva. Također je detaljnije prikazana proizvodnja nodularnog lijeva i postupci cijepljenja taljevine. U eksperimentalnom dijelu rada provedene su kemijska i toplinska analiza te metalografska i mehanička ispitivanja uzoraka nodularnog lijeva. Analizom dobivenih rezultata utvrđeno je da cijepljenje nodularnog lijeva poboljšava metalografska i mehanička svojstva u vidu poboljšanja nodularnosti i povećanja broja nodula izlučenog grafite te porasta vlačne čvrstoće, granice razvlačenja i tvrdoće u odnosu na necijepljeni nodularni lijev.

Abstract

This paper analyzes the influence of inoculation to the changes of metallographic and mechanical properties of ductile iron of EN – GJS – 400 – 15 quality. Three different ductile iron melts are prepared for the needs of the testing. Nodulator Elmag® 3717 is used for the first ductile iron melt test, while the second test used Ultraseed® Ce inoculant as well as Elmag® 3717 nodulator. The third ductile iron test used Elmag® 3717 nodulator and Barinoc® inoculant. The paper consists of theoretical and experimental part. Chemical and heat analysis as well as metallographic and mechanical tests of the ductile iron samples were conducted in the experimental part of the paper. With the analysis of the results obtained it is found that inoculation of ductile iron improves metallographic and mechanical properties like improved nodularity and a higher number of excreted graphite nodules and an increase of tensile strength compared to an uninoculated ductile iron.

Item Type: Thesis (Master's thesis (Bologna))
Uncontrolled Keywords: nodularni lijev, cijepljenje, nodulacija, Ultraseed® Ce, Barinoc®, mikrostruktura, mehanička svojstva, toplinska analiza
Keywords (Croatian): ductile iron, inoculation, nodulation, Ultraseed® Ce, Barinoc®, microstructure, mechanical properties, heat analysis
Subjects: TECHNICAL SCIENCE > Mechanical Engineering
Divisions: 1200 Department of Technology > 1210 Foundry Chair
Date Deposited: 01 Dec 2014 07:54
Last Modified: 20 Apr 2020 08:57
URI: http://repozitorij.fsb.hr/id/eprint/3041

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year