Flexural strength of alumina ceramics: Weibull analysis

Ćurković, Lidija and Bakić, Ante and Kodvanj, Janoš and Haramina, Tatjana (2010) Flexural strength of alumina ceramics: Weibull analysis. = Flexural strength of alumina ceramics: Weibull analysis. Transactions of FAMENA, 34 (1). pp. 13-18. ISSN 1333-1124. Vrsta rada: ["eprint_fieldopt_article_type_article" not defined]. Kvartili JCR: Q4 (2010). Točan broj autora: 4.

FLEXURAL STRENGTH OF ALUMINA CERAMICS.pdf - Published Version Jezik dokumenta:English

Download (441kB) | Preview
Official URL: http://s3.amazonaws.com/academia.edu.documents/411...


In this paper, flexural strength, ofs , of cold isostatically pressed (CIP) high purity alumina ceramics was determined by the three-point bend test. It was found that flexural strength shows a large variation and can be described by a two-parameter Weibull distribution function, with the scale parameter σ0, and the Weibull modulus m. These parameters were determined by the linear regression using the measured values of σfs. It was found that the measured flexural strength, σfs , of alumina ceramics follows the Weibull distribution. The flexural strength values were found to range from 266.7 to 357.5 MPa.

Item Type: Article (["eprint_fieldopt_article_type_article" not defined])
Keywords (Croatian): Alumina ceramics; Flexural strength; Weibull distribution
Subjects: TECHNICAL SCIENCE > Mechanical Engineering
Divisions: 1000 Department of Materials > 1010 Chair of Materials and Tribology
200 Department of Engineering Mechanics > 220 Chair of Experimental Mechanics
Indexed in Web of Science: Yes
Indexed in Current Contents: No
Quartiles: Q4 (2010)
Citations SCOPUS: 1 (17.11.2016.)
Date Deposited: 17 Apr 2015 07:10
Last Modified: 17 Nov 2016 12:57
URI: http://repozitorij.fsb.hr/id/eprint/3589

Actions (login required)

View Item View Item


Downloads per month over past year