Utjecaj opterećenja na izmjerenu tvrdoću silicijeve karbidne keramike

Ćurković, Lidija and Rede, Vera and Grilec, Krešimir (2010) Utjecaj opterećenja na izmjerenu tvrdoću silicijeve karbidne keramike. = Indentation size effect on the hardness of silicon carbide ceramics. Kemija u industriji/Journal of Chemists and Chemical Engineers, 59 (10). pp. 483-488. ISSN 0022-9830. Vrsta rada: ["eprint_fieldopt_article_type_article" not defined]. . Točan broj autora: 3.

Utjecaj opterećenja na izmjerenu tvrdoću silicijeve karbidne keramike.pdf - Published Version Jezik dokumenta:Croatian

Download (579kB) | Preview
Official URL: http://www.scopus.com/inward/record.url?eid=2-s2.0...


The Vickers hardness of CVD SiC ceramics is determined as a function of the indentation load. Vickers hardness pyramid-shaped sharp diamond indenter with angle between opposite faces at an angle of 136° was used to apply five indentation loads of 4.91; 9.81; 29.43; 49.05 and 98.1 N. Care was taken to make indentations only on those areas which had no visible pores. The load was applied at ambient room temperature and dwell time of 15 s. At each indentation load level, 30 perfect indentation were made for CVD SiC ceramics. The results show that the measured hardness depends crucially on the load, which indicates the influence of the indentation size effect (ISE). The load dependence of hardness is analyzed by using the traditional Meyer Law; a proportional specimen resistance (PSR) model and a modified proportional specimen resistance (MPSR) model. The best correlation between measured values and used models is achieved by using the Meyer Law and the modified PSR model. The Meyer index n obtained experimentally is less than 2 (1.7728), which indicates that hardness is dependent on test loads.

Item Type: Article (["eprint_fieldopt_article_type_article" not defined])
Keywords (Croatian): CVD SiC; Diamond indenter; Dwell time; Indentation load; Indentation size effects; Index n; Load dependence; Proportional specimen resistance model; Proportional specimen resistances; Room temperature; Silicon carbide ceramic; Ceramic materials; Indentation; Silicon carbide; Vickers hardness; Vickers hardness testing
Subjects: TECHNICAL SCIENCE > Mechanical Engineering
TECHNICAL SCIENCE > Basic technical sciences
Divisions: 1000 Department of Materials > 1010 Chair of Materials and Tribology
Indexed in Web of Science: No
Indexed in Current Contents: No
Citations SCOPUS: 1 (30.6.2015.)
Date Deposited: 15 Apr 2015 08:44
Last Modified: 26 Aug 2015 12:40
URI: http://repozitorij.fsb.hr/id/eprint/3652

Actions (login required)

View Item View Item


Downloads per month over past year

Nema podataka za dohvacanje citata