Utjecaj pregrijavanja cijevi topničkog oružja na otpornost prema abrazijskom trošenju materijala

Jakopčić, Mirko and Grilec, Krešimir (2011) Utjecaj pregrijavanja cijevi topničkog oružja na otpornost prema abrazijskom trošenju materijala. = Influence of artillery weapon barrel superheat on abrasion wear resistance of material. Tehnički vjesnik : znanstveno-stručni časopis tehničkih fakulteta Sveučilišta u Osijeku, 18 (2). pp. 173-177. ISSN 1330-3651. Kvartili JCR: Q4 (2011). .

[img]
Preview
Text
Dummy article.pdf - Draft Version Jezik dokumenta:English

Download (79kB) | Preview
Official URL: http://www.scopus.com/inward/record.url?eid=2-s2.0...

Abstract

This paper studies the influence of the artillery weapon barrel superheat on abrasion wear resistance of material. The firing process has a compound mechanical, thermal and chemical effect on the barrel. Many wear mechanisms exist in the barrel in firing conditions: abrasion, adhesion, fatigue and tribocorrosion. This paper presents the procedure and the results of abrasion wear experiment. Some test samples were previously tempered and air cooled. The abrasion test samples were made of the heat treated steel 42CrMo4. Wear resistance is represented by the sample mass loss during the wear process. The test results show that unheated samples exhibit higher wear resistance in comparison with heated samples. A significant material wear increase of 43 is shown in the samples which were heated at 900 °C. Conclusively, the test results show that excessive fire causes the weapon barrel to superheat and the material wear resistance to significantly decrease.

Item Type: Article (UNSPECIFIED)
Keywords (Croatian): Abrasion tests; Abrasion wear; Abrasion wear resistance; Artillery weapons; Chemical effect; Fire rate; Firing conditions; Firing process; Mass loss; Material wear; Superheat; Test results; Test samples; Tribo-corrosion; Weapon barrel; Wear mechanisms; Wear process; Abrasion; Fire resistance; Ordnance; Sprayed coatings; Strength of materials; Tribology; Wear resistance
Subjects: TECHNICAL SCIENCE
Divisions: 1000 Department of Materials > 1010 Chair of Materials and Tribology
Indexed in Web of Science: Yes
Indexed in Current Contents: No
Citations JCR: 0 (22.4.2015.)
Quartiles: Q4 (2011)
Citations SCOPUS: 0 (22.4.2015.)
Date Deposited: 22 Apr 2015 11:07
Last Modified: 23 Apr 2015 09:05
URI: http://repozitorij.fsb.hr/id/eprint/3798

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

Nema podataka za dohvacanje citata