Cajner, Franjo and Landek, Darko and Rafel, Hrvoje and Kovačić, Saša (2012) Effect of the heating rate in the tempering of DIN 100 V1. = Effect of the heating rate in the tempering of DIN 100 V1. HTM - Haerterei-Technische Mitteilungen, 67 (2). pp. 118-124. ISSN 0341-101X. Vrsta rada: ["eprint_fieldopt_article_type_article" not defined]. . Točan broj autora: 4.

Full text not available from this repository.
Official URL: http://www.hanser-elibrary.com/doi/abs/10.3139/105...


In this paper, the effect of the heating rate on the process of tempering and the obtained hardness of the DIN 100 V1 (AISI W2) carbon tool steel has been investigated and determined. Steel specimens in two initial states were investigated: after quenching and after quenching and deep-cryogenic cooling. The specimens were submitted to tempering in a dilatometer, varying the heating rates, temperature of tempering between 200 °C and 690 °C and duration of keeping the specimens at that temperature. A common effect of these factors on the temperature of the start of particular stages in tempering and the obtained properties was determined using dilatometry. Diferential dilatation analysis was carried out, together with hardness tests and XRD (X-ray difraction) analysis. © 2012 Carl Hanser Verlag, München.

Item Type: Article (["eprint_fieldopt_article_type_article" not defined])
Keywords (Croatian): Diferential dilatation analysis; Dilatometry; Hardness test; Initial state; Steel specimens; Tempering parameter; XRD; XRD analysis; Carbon tool steels; Carbon; Dilatometers; Hardness; Heating rate; Quenching; Steel research; Tool steel; Tempering
Divisions: 1000 Department of Materials > 1020 Chair of Heat Treatment and Surface Engineering
Indexed in Web of Science: No
Indexed in Current Contents: No
Citations SCOPUS: 0 (08.03.2016.)
Date Deposited: 28 Apr 2015 12:23
Last Modified: 08 Mar 2016 13:49
URI: http://repozitorij.fsb.hr/id/eprint/3943

Actions (login required)

View Item View Item