Inhibition of carbon steel corrosion by imidazoline in carbon dioxide saturated oilfield brine solution

Doležal, Dubravka and Alar, Vesna and Borko, Tihomir (2013) Inhibition of carbon steel corrosion by imidazoline in carbon dioxide saturated oilfield brine solution. = Inhibition of carbon steel corrosion by imidazoline in carbon dioxide saturated oilfield brine solution. Materialwissenschaft und Werkstofftechnik, 44 (7). pp. 626-632. ISSN 0933-5137. Vrsta rada: ["eprint_fieldopt_article_type_article" not defined]. Kvartili JCR: Q4 (2013). Točan broj autora: 3.

[img]
Preview
Text
Inhibition_Alar.pdf Jezik dokumenta:English

Download (491kB) | Preview
Official URL: http://onlinelibrary.wiley.com/doi/10.1002/mawe.20...

Abstract

This work focuses on the testing of imidazoline based corrosion inhibitor and the inhibition of carbon steel corrosion caused by carbon dioxide saturated oilfield brine solution. Electrochemical impedance spectroscopy, linear polarization, anodic and cathodic polarization (Tafel extrapolation method) measurements were carried out. In order to investigate imidazoline based corrosion inhibitor efficiency, carbon dioxide saturated oilfield brine solution without inhibitor and solution with added different concentrations of imidazoline based corrosion inhibitor were tested. Those results were compared. Influence of testing solution temperature and stirring of testing solution on the corrosion inhibitor efficiency were investigated. On the basis of obtained results it can be concluded that optimal concentration of imidazoline based corrosion inhibitor is 50 ppm for the successful and effective corrosion protection of pipelines made of carbon steel under test conditions similar to typical oilfield conditions (35°C, atmospheric pressure, stirring rate 400 min-1).

Item Type: Article (["eprint_fieldopt_article_type_article" not defined])
Keywords (Croatian): Imidazolines; Inhibitor efficiency; Linear polarization; Oilfield brines; Optimal concentration; Solution temperature; Tafel extrapolations; Test condition; Atmospheric pressure; Carbon dioxide; Carbon steel; Cathodic polarization; Efficiency; Electrochemical impedance spectroscopy; Oil fields; Steel corrosion; Corrosion inhibitors
Subjects: TECHNICAL SCIENCE > Mechanical Engineering
Divisions: 1100 Department of Welded Structures > 1120 Chair of Materials Protection
Indexed in Web of Science: Yes
Indexed in Current Contents: Yes
Quartiles: Q4 (2013)
Date Deposited: 07 May 2015 09:08
Last Modified: 15 Feb 2016 15:50
URI: http://repozitorij.fsb.hr/id/eprint/4040

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year