Fatigue growth models for multiple long cracks in plates under cyclic tension based on ΔKI, ΔJ-integral and ΔCTOD parameter

Božić, Željko and Schmauder, Siegfried and Mlikota, Marijo (2012) Fatigue growth models for multiple long cracks in plates under cyclic tension based on ΔKI, ΔJ-integral and ΔCTOD parameter. = Fatigue growth models for multiple long cracks in plates under cyclic tension based on ΔKI, ΔJ-integral and ΔCTOD parameter. Key Engineering Materials, 488-48. pp. 525-528. ISSN 1662-9795. Vrsta rada: ["eprint_fieldopt_article_type_article" not defined]. . Točan broj autora: 3.

[img]
Preview
Text
54e48aa10cf282dbed7008cb.pdf - Published Version Jezik dokumenta:English

Download (1MB) | Preview
Official URL: https://www.researchgate.net/profile/Zeljko_Bozic2...

Abstract

This paper presents the implementation of fatigue crack growth power law equations based on ΔK, ΔJ-integral and ΔCTOD fracture mechanics parameters determined in an FE analysis, to plates with multiple site damage (MSD). Results of fatigue tests with constant amplitude tensile loading carried out on mild steel plate specimens damaged with a single central crack and with three collinear cracks are presented. A relatively larger plastic zone occurred in the crack tip region at higher fatigue crack growth rate (FCGR), from 10-7 to 10-6 m/cycle. The crack growth models based on the elastic-plastic fracture mechanics (EPFM) parameters describe better fatigue crack growth in this range as compared to the liner elastic models.

Item Type: Article (["eprint_fieldopt_article_type_article" not defined])
Keywords (Croatian): fatigue crack growth, multiple cracks, stress intensity factor, J-integral, CTOD
Subjects: TECHNICAL SCIENCE > Aviation, rocket and space technology
Divisions: 1300 Department of Aeronautical Engineering > 1310 Chair of Aerodynamics
Indexed in Web of Science: No
Indexed in Current Contents: No
Date Deposited: 08 Mar 2016 13:25
Last Modified: 08 Mar 2016 13:25
URI: http://repozitorij.fsb.hr/id/eprint/5212

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year