Utjecaj postupaka nitriranja na otpornost trošenju cijevi streljačkog oružja

Mateša, Ivan (2017) Utjecaj postupaka nitriranja na otpornost trošenju cijevi streljačkog oružja. = Influence of nitriding processes on wear resistance of gunbarrels. Undergraduate thesis , Sveučilište u Zagrebu, Fakultet strojarstva i brodogradnje, UNSPECIFIED. Mentor: Jakopčić, Mirko.

[img]
Preview
Text
Matesa_2017_zavrsni_preddiplomski.pdf - Published Version Jezik dokumenta:Croatian

Download (4MB) | Preview
[img] Text
Mateša_Ivan_autorska_izjava_zavrsni_2017.pdf - Published Version
Restricted to Repository staff only Jezik dokumenta:Croatian

Download (473kB)

Abstract (Croatian)

U cijevi vatrenog oružja se tijekom opaljenja razvijaju intezivni, međusobno interaktivni mehanički, toplinski i kemijski tribološki procesi. Materijal cijevi izložen je djelovanju višestrukih mehanizama trošenja materijala, poglavito njezin unutrašnji dio ili kanal cijevi, koji je u izravnom dodiru s projektilom. U radu su proučeni mehanizmi trošenja na različitim metalnim prevlakama. Istraživanje prikazano u ovome radu provedeno je na čeliku za poboljšavanje 32CrMoV12-10, namijenjenom za izradu cijevi naoružanja. Čelik je nabavljen od dva različita proizvođača, a u radu se nastoji ispitati podudarnost njihove tribološke otpornosti u nemodificiranom i modificiranom stanju. Uzorci su razvrstani u dvije grupe: čelik 1 i čelik 2. Obje grupe uzoraka čelika modificirane su postupkom nitriranja u solnoj kupci po jedan uzorak za svaku grupu. Kod ispitivanja otpornosti na trošenje abrazijom, ukupno je ispitano četri uzorka. Za svaku grupu čelika, po jedan uzorak u poboljšanom stanju i po jedan uzorak nitriran u solnoj kupci. Na uzorcima su 2 traga trošenja, s tri ponovljenja mjerenja. Mjeren je gubitak mase uzorka, kao kvantitativni pokazatelj za usporedbu otpornosti ispitnih uzoraka. Pri ispitivanju otpornosti na adhezijsko trošenje, ispitan je po jedan uzorak svake grupe u tri ciklusa (na čeličnom prstenu). Pokazatelj otpornosti je faktor trenja µ, postignut na dodirnoj površini između uzorka i ispitnog prstena

Abstract

Inside a gunbarrel there are complex mechanical, thermal and chemical proccesses during firing. Material of the gunbarrel is exposed to multiple wear mechanisms, especially the inner part of the bore, which is in direct contact with the projectile. Several wear mechanisms, on different types of coatings, are studied in the paper. Research has been done on 32CrMoV12-10 steel which is used as a material for barrel production. Test samples are acquired from the two different manufacturers and are divided in two seperate groups. Samples sre quenched, tempered and stress relief annealed. During the examination of abrasion, four samples wre tested, one of the each group was stress relief anneded and the other was nitrated. Examinations were repeated three times.Mass loss was measured as a quantitive analysis for comparing indices of abrasion. While testing adhesion resistance, one sample of each steel groups was examined in the cycles (on steel test ring). Adhesion resistance index is coefficient of friction µ achieved on the contact surface between test sample and test ring.

Item Type: Thesis (Undergraduate thesis)
Uncontrolled Keywords: cijev, čelik, ispitni uzorci, mehanizmi trošenja
Keywords (Croatian): barrel, steel, test samples, wear machanisms
Subjects: TECHNICAL SCIENCE > Mechanical Engineering
Date Deposited: 24 Feb 2017 08:47
Last Modified: 13 Mar 2017 14:09
URI: http://repozitorij.fsb.hr/id/eprint/7395

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

Nema podataka za dohvacanje citata