Otpornost na abrazijsko trošenje triboloških prevlaka

Grilec, Krešimir (1998) Otpornost na abrazijsko trošenje triboloških prevlaka. = Scientific master's thesis , Sveučilište u Zagrebu, Fakultet strojarstva i brodogradnje, UNSPECIFIED. Mentor: Ivušić, Vinko.

Full text not available from this repository.

Abstract (Croatian)

U ovom radu opisan je mehanizam abrazijskog trošenja te dvije metode koje se koriste za određivanje otpornosti na abrazijsko trošenje: test "suhi pijesak/gumeni kotač" i indeks otpornosti na abrazijsko trošenje. Dan je pregled tvrdih prevlaka koje se nanose na osnovni materijal radi njegove zaštite te su opisani postupci prevlačenja iz parne faze i postupci vrućeg naštrcavanja kojima se danas najčešće nanose tvrde prevlake. U eksperimentalnom dijelu provedena je analiza mikrostrukture prevlaka koje su uključene u znanstveno istraživački projekt Europske komisije COST 516 - Tribologija te je određivana njihova otpornost na abrazijsko trošenje prema normi ASTM G 65-94 (test "suhi pijesak/gumeni kotac"). Osim toga snimljen je tijek abrazijskog trošenja pojedinih prevlaka pri testu "suhi pijesak/gumeni kotač" te je određivan indeks otpornosti na abrazijsko trošenje prevlaka. Ispitivane su sljedeće prevlake: prevlake dobivene difuzijskim postupcima (cementiranje, boriranje, vanadiranje), prevlaka krom nitrida CrN, vruće naštrcane prevlake (Al203, Al203 impregnirana s Al fosfatima), prevlake na osnovi ugljika (DLC - "diamond-like carbon", silicij karbid SiC, višeslojna prevlaka DLC + SiC). Ispitivanja su pokazala da najbolju otpornost na abrazijsko trošenje od ispitivanih prevlaka imaju prevlaka nastala vanadiranjem i CrN prevlaka.

Abstract

The work describes the mechanism of abrasion wear, and two methods used for determining the abrasion resistance: "dry sand/rubber wheel" test and abrasion resistance index. An overview is given on hard layers for the protection of substrate as well as a brief description of chemical and physical vapour deposition and thermal spraying. In the experimental part, the microstructure of layers included in the European research project COST 516 - Tribology, has been analysed and their abrasion resistance has been determined according to the standard ASTM G 65 - 94 ("dry sand/rubber wheel" test). In addition, the process of abrasion wear in "dry sand/rubber wheel" test has been recorded, and the abrasion resistance index determined. The following layers were tested: diffusion layers (case hardening, bonding, vanadising), CrN layer, thermal spray layers (Al203, Al203 layer sealed by Al phosphates), carbon based layers (DLC - diamond-like carbon, SiC, multilayer DLC+SiC). The tests have shown that out of all the tested layers, the best abrasion resistance is that of the layer produced by vanadising and of the CrN layer.

Item Type: Thesis (Scientific master's thesis)
Uncontrolled Keywords: tribologija; inženjerstvo površina; abrazijsko trošenje; indeks otpornosti na abrazijsko trošenje
Divisions: 1000 Department of Materials
Date Deposited: 22 Sep 2014 18:00
Last Modified: 16 Oct 2015 13:20
URI: http://repozitorij.fsb.hr/id/eprint/68

Actions (login required)

View Item View Item

Nema podataka za dohvacanje citata